Physical Properties of Fluoroelastomer Compounds
The physical properties shown below were obtained on molded 0.080″ thick ASTM samples. They are typical of the various compounds but they should not be used to set Quality Control Specification minimum requirements.
Compound | Description |
---|---|
#1035 | 80 Durometer, Acid Resistant, Viton® B |
#1047 | 75 Durometer, Non Specification Fluoroelastomer |
#1055 | 70 Durometer, Non-Black, Non Specification Fluoroelastomer |
#1097 | 70 Durometer, Commercial Grade, Viton® A |
#10116 | 75 Durometer, Low Compression Set, Viton® E-60-C |
#10125 | 60 Durometer, Acid Resistant, Viton® B |
#10131 | 70 Durometer, Non Black, FDA Approved, Viton® A |
#10138 | 75 Durometer, Specification Grade, Viton® A |
#10149 | 55 Durometer, Non Specification Grade, Viton® A |
#10212 | 70 Durometer, Peroxide Cured, Viton® GF |
#10213 | 75 Durometer, Acid Resistant, Viton® B Extrusion |
#10228 | 75 Durometer, Specification Grade Fluoroelastomer |
#10281 | 45 Durometer, Non Specification, Fluoroelastomer |
#10317 | 60 Durometer, Non Specification, Viton® A |
#10320 | 75 Durometer, No Post Cure, Viton® GF |
Compound | Mosites #1035 |
---|---|
Description | 80 Durometer, Acid Resistant, Viton® B |
Hardness (Shore A) | 82 |
Tensile Strength (psi) | 1907 |
Elongation at Break (%) | 277% |
Modulus at 100% Elongation (psi) | 683 |
Tear Strength – Die C Tear (ppi) | 144 |
Specific Gravity | 1.88 |
% Compression Set (22 hours at 350° F) | 30% |
Compound | Mosites #1047 |
---|---|
Description | 75 Durometer, Non Specification Fluoroelastomer |
Hardness (Shore A) | 75 |
Tensile Strength (psi) | 1000 |
Elongation at Break (%) | 200% |
Modulus at 100% Elongation (psi) | 650 |
Tear Strength – Die C Tear (ppi) | 100 |
Specific Gravity | 1.89 |
% Compression Set (22 hours at 350° F) | 36% |
Compound | Mosites #1055 |
---|---|
Description | 70 Durometer, Brown, Non Specification Fluoroelastomer |
Hardness (Shore A) | 72 |
Tensile Strength (psi) | 835 |
Elongation at Break (%) | 232% |
Modulus at 100% Elongation (psi) | 633 |
Tear Strength – Die C Tear (ppi) | 133 |
Specific Gravity | 1.99 |
% Compression Set (22 hours at 350° F) | 44% |
Compound | Mosites #1097 |
---|---|
Description | 70 Durometer, Commercial Grade, Viton® A |
Hardness (Shore A) | 70 |
Tensile Strength (psi) | 1000 |
Elongation at Break (%) | 175% |
Modulus at 100% Elongation (psi) | 600 |
Tear Strength – Die C Tear (ppi) | 125 |
Specific Gravity | 1.97 |
% Compression Set (22 hours at 350° F) | 36% |
Compound | Mosites #10116 |
---|---|
Description | 75 Durometer, Low Compression Set, Viton® E-60-C |
Hardness (Shore A) | 75 |
Tensile Strength (psi) | 1700 |
Elongation at Break (%) | 180% |
Modulus at 100% Elongation (psi) | 1000 |
Tear Strength – Die C Tear (ppi) | 185 |
Specific Gravity | 1.85 |
% Compression Set (22 hours at 350° F) | 7% |
Compound | Mosites #10125 |
---|---|
Description | 60 Durometer, Acid Resistant, Viton® B |
Hardness (Shore A) | 62 |
Tensile Strength (psi) | 2207 |
Elongation at Break (%) | 523% |
Modulus at 100% Elongation (psi) | 242 |
Tear Strength – Die C Tear (ppi) | 118 |
Specific Gravity | 1.90 |
% Compression Set (22 hours at 350° F) | 33% |
Compound | Mosites #10131 |
---|---|
Description | 70 Durometer, Non Black, FDA Approved, Viton® A |
Hardness (Shore A) | 74 |
Tensile Strength (psi) | 1552 |
Elongation at Break (%) | 181% |
Modulus at 100% Elongation (psi) | 773 |
Tear Strength – Die C Tear (ppi) | 131 |
Specific Gravity | 2.15 |
% Compression Set (22 hours at 350° F) | 14% |
Compound | Mosites #10138 |
---|---|
Description | 75 Durometer, Viton® A, Mil R-25897-E, Type II, Class I |
Hardness (Shore A) | 75 |
Tensile Strength (psi) | 1560 |
Elongation at Break (%) | 235% |
Modulus at 100% Elongation (psi) | 682 |
Tear Strength – Die C Tear (ppi) | 131 |
Specific Gravity | 1.88 |
% Compression Set (22 hours at 350° F) | 16% |
Compound | Mosites #10149 |
---|---|
Description | 55 Durometer, Non Specification, Viton® A |
Hardness (Shore A) | 55 |
Tensile Strength (psi) | 1000 |
Elongation at Break (%) | 530% |
Modulus at 100% Elongation (psi) | 175 |
Tear Strength – Die C Tear (ppi) | 85 |
Specific Gravity | 1.68 |
% Compression Set (22 hours at 350° F) | 37% |
Compound | Mosites #10213 |
---|---|
Description | 75 Durometer, Acid Resistant, Viton® B Extrusion |
Hardness (Shore A) | 75 |
Tensile Strength (psi) | 2000 |
Elongation at Break (%) | 295% |
Modulus at 100% Elongation (psi) | 800 |
Tear Strength – Die C Tear (ppi) | 136 |
Specific Gravity | 1.90 |
% Compression Set (22 hours at 350° F) | 60% |
Compound | Mosites #10228 |
---|---|
Description | 75 Duro Fluoroelastomer, Mil-R-83248C, Type II, Class I |
Hardness (Shore A) | 75 |
Tensile Strength (psi) | 1790 |
Elongation at Break (%) | 175% |
Modulus at 100% Elongation (psi) | 1050 |
Tear Strength – Die C Tear (ppi) | 120 |
Specific Gravity | 1.84 |
% Compression Set (22 hours at 350° F) | 10% |
Compound | Mosites #10320 |
---|---|
Description | 75 Durometer, No Post Cure, Viton® GF |
Hardness (Shore A) | 76 |
Tensile Strength (psi) | 2684 |
Elongation at Break (%) | 268% |
Modulus at 100% Elongation (psi) | 741 |
Tear Strength – Die C Tear (ppi) | 130 |
Specific Gravity | 1.81 |
% Compression Set (22 hours at 350° F) | 5% |